What are the classification of resin buttons: The main varieties of resin buttons are roughly divided into four categories, as follows:
The magnetic monochrome button buttons have a single color and no pattern, but they can be made into various shapes.
The flat pearl button product features that the pearl brightness is the same on the entire button surface, like a mirror, bright color, and the appearance of pearl glass button is difficult to distinguish. The natural pearl buttons are mostly used for shirt buckles.
Stick/Plate Mixed Flower This type of product is added with embellishment material to create a variety of desired patterns when pearling. The pearlescent bar can be used as a button that simulates shell effect and various texture patterns.
The production of resin buttons (unsaturated polyester) can be divided into two broad categories: panel buttons and stick buttons.
1. Raw materials: Unsaturated polyester is a raw material extracted from petroleum, transparent and viscous liquid. Resins with catalysts and hardeners can be added with different colorants, or other raw materials, such as wax, salt, sawdust, straw, etc., with different amounts of raw materials, at different concentrations, different temperatures, different rotation speeds and special Under the cooperation of accessories, it will produce ever-changing patterns, and it is also an important material for imitation of natural reproduction pearls, horns, fruits, wood grain, stone, marble and other natural imitation buttons.
2. Plate: Pour the completely mixed resin into the rotating bucket, commonly called the rewind bucket or large diameter, and pour on multiple layers as required. After about 30 minutes, the resin in the bucket is soft and gelatinous due to the chemical reaction. Cut into plate shape and place it on the punching machine to flush out the knob. A plate rushes out of the 14L button embryo 126 锣.
3, stick flowers: The completely mixed glue, through a special swing into the waxed aluminum tube, until the glue into a soft gel pulled out of the aluminum tube in the glue stick immediately sliced, slicing knife can be cut every 1300 18L button knob embryo. Each stick can be cut into 24L button embryos 2 锣.
4. Stick embryos: All blank embryos or stick embryos are soft and must be placed in hot water at 80 degrees for 10 hours to speed up the chemical reaction. After the complete reaction, embryos are hard embryos.
5, car button: automatic car button machine, you can once over the car, car and drilling, even if the lettering, carved flowers can be completed in one go. Ordinary four holes have a side and a button on the bottom of the car, and 100 grains per minute can be carved, the same as the embryo and stick embryo.
6. Grinding: As the surface of the car and the bottom of the car leave marks, it is necessary to put it into a water mill barrel. The slow-rotating water mill bucket is mainly filled with water and lime powder. This process takes ten hours. After the water has been rubbed, the button has a dull mist effect. If the lighting effect needs to be brightened, the bamboo core and wax are mainly put in the brightening barrel. This process takes 20 hours; or the small stones and stone powder are used in the water polishing machine. To achieve the above effect, this process takes 15 hours.
For more information, please update: China Button Industry Network